THE EFFECT OF Nano-MgO ON THE MECHANICAL AND FLAMMABILITY PROPERTIES OF HYBRID NANO COMPOSITES FROM WOOD FLOUR-POLYETHYLENE
No hay miniatura disponible
Fecha
Título de la revista
ISSN de la revista
Título del volumen
Editor
Universidad del Bío Bío
Resumen
Descripción
ParameteThis study considered the effect of nanomagnesium oxide on the mechanical and flammability features of composites made of wood flour and high-density polyethylene. A sample of wood flour was made from the mixture of hardwoods and high density polyethylene with the weight ratio of 50%. Maleic anhydride was added as a compatibilizer (2 phc), and nanomagnesium oxide was applied at 6 levels (0, 1, 2, 3, 4, 5 phc). These materials were mixed, and samples were prepared with determined sizes by injection molding machine. The samples were subjected to flexural tests to examine the mechanical features, and to study flammability strength, various tests were conducted with a cone calorimeter, including the amount of char residue, total smoke production, time to ignition, and heat release rate, according to ASTM E1354-92 (1992). The addition of up to 3 phc nanomagnesium oxide increased flexural strength and modulus, but further additions decreased these values. The addition of 5 phc nanomagnesium oxide increased the char residue and ignition time, and it decreased the heat release rate, total smoke production, and burning rate. Scanning electron microscopy and energy dispersive X-ray (EDX) analysis indicated the improper transmittance of nanomagnesium oxide and accumulations in the samples.s characterizing wood and air were studied in order to analyze the performance of a wood solar dryer functioning under Moroccan climate. A mathematical model based on the climate data of Rabat city was used to investigate theoretically the wood drying process. Two wood species- thuya ( Tetraclinis articulate ) and pine ( Pinus pinaster )-were examined in the present study. The results obtained by computer simulations are in good agreement with the experimental values. Furthermore, our findings indicate that the use of a global mass transfer coefficient for low temperature convective and homogenous drying conditions allows the influence of the principal operating parameters (wood thickness, wood density, air temperature, air velocity and ventilation mode) on the drying time to be estimated with great accuracy. Analyses pertaining to the two studied wood species revealed that(1) pine dries more quickly than thuya, (2) the drying process is faster in the summer relative to other seasons, (3) increasing the air velocity by 100% results in a 20% reduction in the drying time, and (4) continued ventilation reduces the drying time by 43%.|
Palabras clave
Agrociencias